E410-16 Stainless Steel Welding Rod (CHK202)
E410-16 welding rod is suitable for welding stainless steel structures that fabricated by 06Cr13 and 12Cr13 ferritic stainless steels. Also, it could surface workpiece for wear-resisting or corrosion-resisting.
Type of Covering: Lime-titania
Welding Position: F, H, HF, OH, V
Type of Current: DCEP or AC
Notice:
- The rod should be baked at 250℃ for 1 hour before use.
- The surfaces to be welded must be cleaned away impurities of oil contamination, moisture and so on.
- The weldment should be preheated to 250℃-350℃ before welding.
E410-16 Chemical Composition of Deposited Metal (%)
| C | Mn | Si | P | S | Ni | Cr | Mo | Cu | |
|---|---|---|---|---|---|---|---|---|---|
| Standard | ≤0.12 | ≤1.0 | ≤0.90 | ≤0.04 | ≤0.03 | ≤0.70 | 11.0-14.0 | ≤0.75 | ≤0.75 |
| Typical | 0.035 | 0.14 | 0.33 | 0.025 | 0.01 | 0.38 | 12.10 | 0.016 | 0.033 |
Mechanical Properties of Deposited Metal (PWHT)
The test specimen is heated to 860℃, hold for 2 hours, furnace cool to 600℃, and air cool to ambient.
| Tensile Strength Rm (MPa) | Elongation A4 (%) | |
|---|---|---|
| Standard | ≥450 | ≥15 |
| Typical | 560 | 22 |
Sizes & Recommended Current (DC+ or AC)
| E410-16 Welding Rod Diameter (mm) | 2.5 | 3.2 | 4.0 | 5.0 |
|---|---|---|---|---|
| Welding Rod Length (mm) | 250 | 300 | 350 | 350 |
| Welding Current (A) | 60-80 | 80-120 | 100-160 | 150-200 |