E316L-16 Welding Rod (CHS022)
E316L-16 welding rod is suitable for welding facilities of synthetic fibre or urea, as well as for similar stainless steel structures. Also, it could be used for welding structures made by category of chromium stainless steels that could not be PWHT or for welding dissimilar steels and ply steels. The weld metal has good performance of resistance to corrosion, heat and crack defect.
Type of Covering: Lime-titania
Welding Position: F, H, HF, OH, V
Type of Current: DCEP or AC
E316L-16 Chemical Composition of Deposited Metal (%)
C | Mn | Si | P | S | Ni | Cr | Mo | Cu | |
---|---|---|---|---|---|---|---|---|---|
Standard | ≤0.04 | 0.5-2.5 | ≤1.00 | ≤0.04 | ≤0.03 | 11.0-14.0 | 17.00-20.00 | 2.0-3.0 | ≤0.75 |
Typical | 0.030 | 0.85 | 0.76 | 0.023 | 0.012 | 11.86 | 19.00 | 2.50 | 0.16 |
Mechanical Properties of Deposited Metal (AW)
Tensile Strength Rm (MPa) | Elongation A4 (%) | |
---|---|---|
Standard | ≥490 | ≥25 |
Typical | 575 | 44 |
Sizes & Recommended Current (DC+ or AC)
E316L-16 Welding Rod Diameter (mm) | 2.0 | 2.5 | 3.2 | 4.0 | 5.0 |
---|---|---|---|---|---|
Welding Rod Length (mm) | 300 | 300 | 350 | 350 | 350 |
F, H Welding Current (A) | 30-50 | 50-85 | 85-120 | 120-160 | 150-200 |
V, OH Welding Current (A) | 30-50 | 50-70 | 70-100 | 90-135 |