E316-16 ISO ES316-16 Welding Rod (CHS202)

E316-16 welding rod is used for welding structures fabricated by 06Cr17Ni12Mo2 stainless steel, which work in mediums of organic acid or inorganic acid (non-oxidizing acid). It is suitable for flat welding and fillet welding on sheets and it could be applied for welding structures made by category of high chromium steels that could not be PWHT or for dissimilar steels welding. The weld metal has good performance of corrosion-resisting, heat-resisting and crack-resisting, especially resistance to corrosion of chloridion.

Type of Covering: Lime-titania

Welding Position: F, H, HF, OH, V

Type of Current: DCEP or AC

Notice:

  • The rod should be baked at 300℃-350℃ for 1 hour before use.
  • The surfaces to be welded must be cleaned away impurities of oil contamination, rust, moisture and so on.
  • Smaller current and short arc are recommended in welding and weave beads no wider than 2.5 times of the diameter of the core rod is better.

E316-16 Chemical Composition of Deposited Metal (%)

 CMnSiPSNiCrMoCu
Standard≤0.080.5-2.5≤1.00≤0.04≤0.0311.0-14.017.0-20.02.0-3.0≤0.75
Typical0.0370.820.760.0280.01311.8318.812.400.19

Mechanical Properties of Deposited Metal (AW)

 Tensile Strength Rm (MPa)Elongation A4 (%)
Standard≥520≥25
Typical57542

Sizes & Recommended Current (DC+ or AC)

E316-16 Welding Rod Diameter (mm)2.02.53.24.05.0
Welding Rod Length (mm)300300350350350
F, H Welding Current (A)30-5050-8585-120120-160150-200